Systems and methods for forming metal oxides using metal diketonates and/or ketoimines

ABSTRACT

A method of forming (and an apparatus for forming) a metal oxide layer on a substrate, particularly a semiconductor substrate or substrate assembly, using a vapor deposition process and one or more precursor compounds that include diketonate ligands and/or ketoimine ligands.

This is a continuation of application Ser. No. 10/230,193, filed Aug. 28, 2002, (pending), which is incorporated herein by reference in its entirety.

FIELD OF THE INVENTION

This invention relates to methods of forming a metal oxide layer on a substrate using one or more precursor compounds that include one or more diketonate ligands and/or ketoimine ligands during a vapor deposition process. The precursor compounds and methods are particularly suitable for the formation of metal oxide layers on semiconductor substrates or substrate assemblies.

BACKGROUND OF THE INVENTION

The continuous shrinkage of microelectronic devices such as capacitors and gates over the years has led to a situation where the materials traditionally used in integrated circuit technology are approaching their performance limits. Silicon (i.e., doped polysilicon) has generally been the substrate of choice, and silicon dioxide (SiO₂) has frequently been used as the dielectric material with silicon to construct microelectronic devices. However, when the SiO₂ layer is thinned to 1 nm (i.e., a thickness of only 4 or 5 molecules), as is desired in the newest micro devices, the layer no longer effectively performs as an insulator due to the tunneling current running through it.

Thus, new high dielectric constant materials are needed to extend device performance. Such materials need to demonstrate high permittivity, barrier height to prevent tunneling, stability in direct contact with silicon, and good interface quality and film morphology. Furthermore, such materials must be compatible with the gate material, electrodes, semiconductor processing temperatures, and operating conditions.

High quality thin oxide films of metals, such as ZrO₂, HfO₂, Al₂O₃, and YSZ deposited on semiconductor wafers have recently gained interest for use in memories (e.g., dynamic random access memory (DRAM) devices, static random access memory (SRAM) devices, and ferroelectric memory (FERAM) devices). These materials have high dielectric constants and therefore are attractive as replacements in memories for SiO₂ where very thin layers are required. These metal oxide layers are thermodynamically stable in the presence of silicon, minimizing silicon oxidation upon thermal annealing, and appear to be compatible with metal gate electrodes. Specifically, for gate dielectrics, La₂O₃, HfO₂, and ZrO₂ are also promising as they possess relatively high values for permittivity and bandgap.

This discovery has led to an effort to investigate various deposition processes to form layers, especially dielectric layers, based on metal oxides. Such deposition processes have included vapor deposition, metal thermal oxidation, and high vacuum sputtering. Vapor deposition processes, which includes chemical vapor deposition (CVD) and atomic layer deposition (ALD), are very appealing as they provide for excellent control of dielectric uniformity and thickness on a substrate. But vapor deposition processes typically involve the co-reaction of reactive metal precursor compounds with an oxygen source such as oxygen or water, either of which can cause formation of an undesirable SiO₂ interfacial layer. Thus, an effort is underway to develop water- and oxygen-free vapor deposition processes.

Ritala et al., “Atomic Layer Deposition of Oxide Thin Films with Metal Alkoxides as Oxygen Sources,” SCIENCE, 288:319-321 (2000) describe a chemical approach to ALD of thin oxide films. In this approach, a metal alkoxide, serving as both a metal source and an oxygen source, reacts with another metal compound such as a metal chloride or metal alkyl to deposit a metal oxide on silicon without creating an interfacial silicon oxide layer. In some cases, the use of a metal alkoxide is not practical, particularly for low valent metals. For example, the alkoxides are not sufficiently volatile for vapor deposition processes.

Despite these continual improvements in semiconductor dielectric layers, there remains a need for a vapor deposition process utilizing sufficiently volatile metal precursor compounds that can form a thin, high quality oxide layer, particularly on a semiconductor substrate using a vapor deposition process.

SUMMARY OF THE INVENTION

This invention provides methods of forming a metal oxide layer on a substrate, particularly a semiconductor substrate or substrate assembly, using a vapor deposition technique. The methods involve forming the layer by combining one or more metal diketonate and/or ketoimine precursor compounds with one or more other metal-containing precursor compounds. The latter precursor compounds, for example, are typically metal halides, metal alkyls, metal organo amines, or combinations thereof. Significantly, the methods of the present invention do not require the use of water or a strong oxidizer, thus reducing (and typically avoiding) the problem of producing an undesirable interfacial oxide layer between the desired oxide layer and the substrate. The diketonate and/or ketoimine precursors can be the oxygen source for the metal oxide films.

The methods of the present invention involve forming a metal oxide layer on a substrate by reacting one or more metal precursor compounds the formula L_(n)M¹O_(x)(keto)_(y) (Formula I) with one or more metal precursor compounds of the formula M²Y_(z) (Formula II). In Formulas I and II: M¹ and M² are each independently a metal (preferably, main group metal (including metalloids or semimetals), transition metal, or lanthanide); each “keto” is independently a diketonate or ketoimine ligand; each L group is a neutral or anionic (e.g., monoanionic or dianionic) supporting ligand; each Y group is independently a halogen (X), R¹, or an amine of the formula (NR²R³), wherein each R¹, R², and R³ is independently hydrogen or an organic group; n=0 to 5 (preferably, 0 to 2); x is 0 to 3; y is 1 to 5 and is dependent on the oxidation state of M¹ and on the value of n; z is at least one and is dependent on the oxidation state of M². In one preferred embodiment the compound of Formula II includes both halogen atoms and hydrogen or and organic groups and is of the formula M²X_(f)R¹ _(s), wherein r+s is dependent on the oxidation state of the metal.

The resultant oxide layer may include one (i.e., M¹ =M²) or more different metals (preferably, two metals) and is preferably of the formula M¹M²O_(m) (Formula III), wherein M¹ and M² are as defined above, and m is at least one and is dependent on the oxidation state(s) of the metal(s).

In one embodiment, the present invention provides a method of forming a metal oxide layer on a substrate (e.g., as in a process of manufacturing a semiconductor structure). The method includes: providing a substrate (e.g., semiconductor substrate or substrate assembly); providing at least one precursor compound of the formula L_(n)M¹O_(x)(keto)_(y) (Formula I) and at least one precursor compound of the formula M²Y_(z)(Formula II) as defined above; and contacting the precursor compounds to form a metal oxide layer on the substrate (e.g., one or more surfaces of the semiconductor substrate or substrate assembly) using a vapor deposition process.

In another embodiment, the present invention provides a method of forming a metal oxide layer on a substrate (e.g., as in a process of manufacturing a semiconductor structure). The method includes: providing a substrate (e.g., a semiconductor substrate or substrate assembly) within a deposition chamber; providing at least one precursor compound of the formula L_(n)M¹O_(x)(keto)_(y) (Formula I) and at least one precursor compound of the formula M²Y_(z)(Formula II) as defined above; and vaporizing the precursor compounds to form vaporized precursor compounds; and directing the vaporized precursor compounds to the substrate to form a metal oxide layer (e.g., dielectric layer) on one or more surfaces of the substrate.

In yet another embodiment, the present invention provides a method of manufacturing a memory device structure. The method includes: providing a substrate having a first electrode thereon; providing at least one precursor compound of the formula L_(n)M¹O_(x)(keto)_(y) (Formula I) and at least one precursor compound of the formula M²Y_(z)(Formula II) as defined above; and vaporizing the precursor compounds to form vaporized precursor compounds; directing the vaporized precursor compounds to the substrate to form a metal oxide dielectric layer on the first electrode of the substrate; and forming a second electrode on the dielectric layer.

The methods of the present invention can utilize a chemical vapor deposition (CVD) process, which can be pulsed, or an atomic layer deposition (ALD) process (a self-limiting vapor deposition process that includes a plurality of deposition cycles, typically with purging between the cycles). Preferably, the methods of the present invention use ALD. For certain ALD processes, the precursor compounds can be alternately introduced into a deposition chamber during each deposition cycle.

The present invention also provides a vapor deposition apparatus that includes: a vapor deposition chamber having a substrate positioned therein; one or more vessels comprising one or more precursor compounds having the formula L_(n)M¹O_(x)(keto)_(y) (Formula I); and one or more vessels comprising one or more one precursor compounds of the formula M²Y_(z)(Formula II).

“Semiconductor substrate” or “substrate assembly” as used herein refers to a semiconductor substrate such as a base semiconductor layer or a semiconductor substrate having one or more layers, structures, or regions formed thereon. A base semiconductor layer is typically the lowest layer of silicon material on a wafer or a silicon layer deposited on another material, such as silicon on sapphire. When reference is made to a substrate assembly, various process steps may have been previously used to form or define regions, junctions, various structures or features, and openings such as capacitor plates or barriers for capacitors.

“Layer” as used herein refers to any metal-containing layer that can be formed on a substrate from the precursor compounds of this invention using a vapor deposition process. The term “layer” is meant to include layers specific to the semiconductor industry, such as “barrier layer,” “dielectric layer,” and “conductive layer.” (The term “layer” is synonymous with the term “film” frequently used in the semiconductor industry.) The term “layer” is also meant to include layers found in technology outside of semiconductor technology, such as coatings on glass.

“Precursor compound” as used herein refers to a metal diketonate, metal ketoimine compound, metal halide, metal organo-amine, metal alkyl, for example, capable of forming, either alone or with other precursor compounds, a metal oxide layer on a substrate in a vapor deposition process.

“Deposition process” and “vapor deposition process” as used herein refer to a process in which a metal-containing layer is formed on one or more surfaces of a substrate (e.g., a doped polysilicon wafer) from vaporized precursor compound(s). Specifically, one or more metal precursor compounds are vaporized and directed to one or more surfaces of a heated substrate (e.g., semiconductor substrate or substrate assembly) placed in a deposition chamber. These precursor compounds form (e.g., by reacting or decomposing) a non-volatile, thin, uniform, metal-containing layer on the surface(s) of the substrate. For the purposes of this invention, the term “vapor deposition process” is meant to include both chemical vapor deposition processes (including pulsed chemical vapor deposition processes) and atomic layer deposition processes.

“Chemical vapor deposition” (CVD) as used herein refers to a vapor deposition process wherein the desired layer is deposited on the substrate from vaporized metal precursor compounds (and any reaction gases used) within a deposition chamber with no effort made to separate the reaction components. In contrast to a “simple” CVD process that involves the substantial simultaneous use of the precursor compounds and any reaction gases, “pulsed” CVD alternately pulses these materials into the deposition chamber, but does not rigorously avoid intermixing of the precursor and reaction gas streams, as is typically done in atomic layer deposition or ALD (discussed in greater detail below).

“Atomic layer deposition” (ALD) as used herein refers to a vapor deposition process in which numerous consecutive deposition cycles are conducted in a deposition chamber. Typically, during each cycle the metal precursor is chemisorbed to the substrate surface; excess precursor is purged out; a subsequent precursor and/or reaction gas is introduced to react with the chemisorbed layer; and excess reaction gas (if used) and by-products are removed. As compared to the one cycle chemical vapor deposition (CVD) process, the longer duration multi-cycle ALD process allows for improved control of layer thickness by self-limiting layer growth and minimizing detrimental gas phase reactions by separation of the reaction components. The term “atomic layer deposition” as used herein is also meant to include the related terms “atomic layer epitaxy” (ALE), molecular beam epitaxy (MBE), gas source MBE, organometallic MBE, and chemical beam epitaxy when performed with alternating pulses of precursor compound(s), reaction gas(es), and purge (i.e., inert carrier) gas.

“Chemisorption” as used herein refers to the chemical adsorption of vaporized reactive precursor compounds on the surface of a substrate. The adsorbed species are irreversibly bound to the substrate surface as a result of relatively strong binding forces characterized by high adsorption energies (e.g., >30 kcal/mol), comparable in strength to ordinary chemical bonds. The chemisorbed species typically form a mononolayer on the substrate surface. (See “The Condensed Chemical Dictionary”, 10th edition, revised by G. G. Hawley, published by Van Nostrand Reinhold Co., New York, 225 (1981)). The technique of ALD is based on the principle of the formation of a saturated monolayer of reactive precursor molecules by chemisorption. In ALD one or more appropriate precursor compounds or reaction gases are alternately introduced (e.g., pulsed) into a deposition chamber and chemisorbed onto the surfaces of a substrate. Each sequential introduction of a reactive compound (e.g., one or more precursor compounds and one or more reaction gases) is typically separated by an inert carrier gas purge. Each precursor compound co-reaction adds a new atomic layer to previously deposited layers to form a cumulative solid layer. The cycle is repeated, typically for several hundred times, to gradually form the desired layer thickness. It should be understood that ALD can alternately utilize one precursor compound, which is chemisorbed, and one reaction gas, which reacts with the chemisorbed species.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-3 are exemplary capacitor constructions.

FIG. 4 is a perspective view of a vapor deposition coating system suitable for use in the method of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION

The present invention provides methods of forming a metal oxide layer (preferably a mixed metal oxide layer) on a substrate (preferably a semiconductor substrate or substrate assembly). The methods of the present invention involve forming a metal oxide layer on a substrate by combining one or more metal precursor compounds the formula L_(n)M¹O_(x)(keto)_(y) (Formula I) with one or more metal precursor compounds of the formula M²Y_(z)(Formula II). In Formulas I and II: M¹ and M² are each independently a metal (preferably, main group metal (including metalloids or semimetals), transition metal, or lanthanide); each “keto” is independently a diketonate or ketoimine ligand; each L group is a neutral or anionic (e.g., monoanionic or dianionic) supporting ligand; each Y group is independently a halogen (X), R¹, or an amine of the formula (NR²R³), wherein each R¹, R², and R³ is independently hydrogen or an organic group; n is 0 to 5 (preferably, 0 to 2); x is 0 to 3; y is 1 to 5 and is dependent on the oxidation state of M¹ and on the value of n; z is at least one and is dependent on the oxidation state of M². In one preferred embodiment the compound of Formula II includes both halogen atoms and hydrogen or and organic groups and is of the formula M²X_(r)R¹ _(s), wherein r+s is dependent on the oxidation state of the metal.

The metal oxide layer may include one or more different metals and is preferably of the formula M¹M²O_(m) (Formula III), wherein M¹ and M² are as defined above, and m is at least one and is dependent on the oxidation state(s) of the metal(s). For certain embodiments M¹ and M² are the same metals. For embodiments in which there are more than one metal, the ratio of metals can be controlled by the ratio of the starting materials of Formulas I and II. Alternatively, a metal-containing compound of a formula other than Formulas I and II can be used to add other metals or adjust the amount of one of the metals provided by Formulas I and II. Preferably, the metal oxide layer is a mixed metal oxide. More preferably, the metal oxide layer includes two metals (e.g., Y and Al or Ba and Ti).

The substrate on which the metal oxide layer is formed is preferably a semiconductor substrate or substrate assembly. Any suitable semiconductor material is contemplated, such as for example, conductively doped polysilicon (for this invention simply referred to as “silicon”). A substrate assembly may also contain a layer that includes platinum, iridium, rhodium, ruthenium, ruthenium oxide, titanium nitride, tantalum nitride, tantalum-silicon-nitride, silicon dioxide, aluminum, gallium arsenide, glass, etc., and other existing or to-be-developed materials used in semiconductor constructions, such as dynamic random access memory (DRAM) devices and static random access memory (SRAM) devices, for example.

Substrates other than semiconductor substrates or substrate assemblies can be used in methods of the present invention. These include, for example, fibers, wires, etc. If the substrate is a semiconductor substrate or substrate assembly, the layers can be formed directly on the lowest semiconductor surface of the substrate, or they can be formed on any of a variety of the layers (i.e., surfaces) as in a patterned wafer, for example.

The precursor compounds useful in this invention are of the formulas L_(n)M¹O_(x)(keto)_(y) (Formula I) and M²Y_(z) (Formula II). These compound can include organic groups (as described in greater detail below).

As used herein, the term “organic group” is used for the purpose of this invention to mean a hydrocarbon group that is classified as an aliphatic group, cyclic group, or combination of aliphatic and cyclic groups (e.g., alkaryl and aralkyl groups). In the context of the present invention, suitable organic groups for precursor compounds of this invention are those that do not interfere with the formation of a metal oxide layer using vapor deposition techniques. In the context of the present invention, the term “aliphatic group” means a saturated or unsaturated linear or branched hydrocarbon group. This term is used to encompass alkyl, alkenyl, and alkynyl groups, for example. The term “alkyl group” means a saturated linear or branched monovalent hydrocarbon group including, for example, methyl, ethyl, n-propyl, isopropyl, t-butyl, amyl, heptyl, and the like. The term “alkenyl group” means an unsaturated, linear or branched monovalent hydrocarbon group with one or more olefinically unsaturated groups (i.e., carbon-carbon double bonds), such as a vinyl group. The term “alkynyl group” means an unsaturated, linear or branched monovalent hydrocarbon group with one or more carbon-carbon triple bonds. The term “cyclic group” means a closed ring hydrocarbon group that is classified as an alicyclic group, aromatic group, or heterocyclic group. The term “alicyclic group” means a cyclic hydrocarbon group having properties resembling those of aliphatic groups. The term “aromatic group” or “aryl group” means a mono- or polynuclear aromatic hydrocarbon group. The term “heterocyclic group” means a closed ring hydrocarbon in which one or more of the atoms in the ring is an element other than carbon (e.g., nitrogen, oxygen, sulfur, etc.).

As a means of simplifying the discussion and the recitation of certain terminology used throughout this application, the terms “group” and “moiety” are used to differentiate between chemical species that allow for substitution or that may be substituted and those that do not so allow for substitution or may not be so substituted. Thus, when the term “group” is used to describe a chemical substituent, the described chemical material includes the unsubstituted group and that group with nonperoxidic O, N, S, Si, or F atoms, for example, in the chain as well as carbonyl groups or other conventional substituents. Where the term “moiety” is used to describe a chemical compound or substituent, only an unsubstituted chemical material is intended to be included. For example, the phrase “alkyl group” is intended to include not only pure open chain saturated hydrocarbon alkyl substituents, such as methyl, ethyl, propyl, t-butyl, and the like, but also alkyl substituents bearing further substituents known in the art, such as hydroxy, alkoxy, alkylsulfonyl, halogen atoms, cyano, nitro, amino, carboxyl, etc. Thus, “alkyl group” includes ether groups, haloalkyls, nitroalkyls, carboxyalkyls, hydroxyalkyls, sulfoalkyls, etc. On the other hand, the phrase “alkyl moiety” is limited to the inclusion of only pure open chain saturated hydrocarbon alkyl substituents, such as methyl, ethyl, propyl, t-butyl, and the like.

In Formulas I and II: M¹ and M² are each independently a metal (preferably, main group metal (including metalloids or semimetals), transition metal, or lanthanide). For certain methods of the present invention, preferably, M¹ and M² are each independently selected from the group of metals (including metalloids or semimetals) of Groups IIA, IIIA, IVA, IVB, VA, VB, VIIIB, IB, and the lanthanides (i.e., Groups 2, 4, 5, 8-11, 13, 14, 15, and the lanthanides). More preferably, M¹ and M² are each independently selected from the group of Sr, Ba, Y, the lanthanides, Ti, Zr, Hf, Nb, Ta, Al, Si, and mixtures thereof. Even more preferably, M¹ and M² are each independently selected from the group of Sr, Ba, Y, La, Ce, Pr, Gd, Ti, Al, Si, and mixtures thereof. Most preferably, M¹ and M² are each independently selected from the group of La, Ce, Pr, Gd, Al, Si, and mixtures thereof.

In Formula I, there can be up to 5 L ligands (i.e., n=0-5), and preferably up to 2 L ligands (i.e., n=0-2). More preferably, L is absent (x=0). Each L group is a neutral or anionic (e.g., monoanionic or dianionic) supporting ligand. If one ore more L ligands are present, they are selected from the group of dialkyl- and trialkyl-amines, polyamines (e.g., N,N,N′N′N″-pentamethyldiethylenetriamine, diethylenetriamine), trialkylphosphines, ethers (including linear, branched, and cyclic ethers and polyethers), unsubstituted and fluoro-substituted alkyls (including linear, branched, and cyclic alkyls), unsubstituted alkenes (including linear, branched, and cyclic monoenes, dienes, and trienes, such as cyclopentadienyl and cyclooctadienyl), unsubstituted alkynes (including linear, branched, and cyclic alkynes), alkoxy groups (e.g., methoxy, ethoxy, isopropoxy), carboxylates, thiolates, substituted silanes (including alkoxy substituted silanes, alkyl substituted silanes, alkenyl substituted silanes), as well as oxo, nitrile, isonitrile, and carbonyl ligands. Various combinations of such L groups can be present in a molecule.

In Formula I, there is at least 1 “keto” ligand (i.e., y=1-5). Typically, the number of “keto” ligands is dependent on the oxidation state of M¹ and on the value of n. Each “keto” ligand is independently a diketonate or ketoimine ligand. Preferably, there are 2-3 “keto” ligands per metal (i.e., y=2-3). Preferably the “keto” ligand is of the formula (Formula IV):

wherein Z is O or NR⁷ and each R⁴, R⁵, R⁶, and R⁷ is independently hydrogen or an organic group. Preferably, each of the organic groups contains 1-10 carbon atoms, more preferably, 1-6 carbon atoms, and most preferably, 1-4 carbon atoms. More preferably, the “keto” ligand is a diketonate wherein Z is O (oxygen).

In the “keto” ligands of Formula IV, more preferably, each R⁴, R⁵, R⁶, and R⁷ is independently H, or an organic group optionally containing one or more heteroatoms (e.g., oxygen or nitrogen), fluorine atoms, or functional groups (e.g., a carbonyl group, a hydroxycarbyl group, or an aminocarbyl group). That is, included within the scope of Formula IV are ligands wherein at least one R⁴, R⁵, R⁶, and R⁷ is an organic group and at least one carbon atom is replaced with one of a carbonyl group, a hydroxycarbyl group, an oxygen atom, a nitrogen atom, or an aminocarbyl group. Also included within the scope of Formula IV are compounds wherein at least one R⁴, R⁵, R⁶, and R⁷ is an organic group and at least one hydrogen atom in the organic group is replaced with a fluorine atom. Most preferably, the organic groups of Formula IV are (C1-C4)alkyl groups, which may be a linear, branched, or cyclic, as well as alkenyl groups (e.g., dienes and trienes), or alkynyl groups. In any of these groups, one or more of the hydrogen atoms can be replaced by fluorine atoms. Of these, the organic groups are preferably trifluoromethyl or tert-butyl. In one preferred embodiment, at least R⁵ is hydrogen. More preferably, R⁵ is hydrogen and R⁴ and R⁶ are tert-butyl. More preferably, R⁷ is methyl.

In Formula II, there is at least one Y group (i.e., z is at least one and is dependent on the oxidation state of M²), which can be a halogen (X) (preferably, F, Cl, Br, or I, and more preferably, Cl, Br, I, and most preferably, Cl), R¹, or an amine of the formula (NR²R³), wherein each R¹, R², and R³ is independently hydrogen or an organic group. Preferably, each of the organic groups of R¹, R², and R³ contain 1-10 carbon atoms, more preferably, 1-6 carbon atoms, and most preferably, 1-4 carbon atoms. Preferably, at least one Y is a halogen or R¹ wherein R¹ is an organic group, and more preferably, every Y is R¹ wherein R¹ is hydrogen or an organic group.

In the Y groups of Formula II, each R¹, R², and R³ is independently hydrogen or an organic group optionally containing one or more heteroatoms (e.g., oxygen or nitrogen), fluorine atoms, or functional groups (e.g., a carbonyl group, a hydroxycarbyl group, or an aminocarbyl group). That is, included within the scope of the compounds of Formula II are compounds wherein at least one R¹, R², and R³ is an organic group with at least one carbon atom in the organic group replaced with one of a carbonyl group, a hydroxycarbyl group, an oxygen atom, a nitrogen atom, or an aminocarbyl group. Also included within the scope of the compounds of Formula II are compounds wherein at least one R¹, R², and R³ is an organic group and at least one hydrogen atom in the organic group is replaced with a fluorine atom. Most preferably, the organic groups of Formula II are (C1-C4)alkyl groups, which may be a linear or branched groups, as well as alkenyl groups (e.g., dienes and trienes), or alkynyl groups. In any of these organic groups, one or more of the hydrogen atoms can be replaced by fluorine atoms. Of these, the organic groups are preferably methyl moieties or cyclopentadienyl groups (substituted or unsubstituted). In one preferred embodiment, at least one R¹, R², and R³ is methyl. More preferably, any R¹, R², and R³ present is methyl (Me).

Examples of compounds of Formula I include Sr(thd)₂, Ba(thd)₂, La(thd)₂, Y(thd)₂, Ce(thd)₂, and TiO(thd)₂, wherein thd is tetramethylheptanedionate. Examples of compounds of Formula II include Al(CH₃)₃, Al(CH₂CH₃)₃, TiCl₄, Ti(NMe₂)₄, SiCl₄, TaF₅, and Si(NMe₂)₄.

The complexes of the present invention can be prepared by a variety of methods known to one of skill in the art. For example, complexes of Formula I can be prepared by reaction of a metal hexamethyldisilazide with appropriate equivalents of a dione such as 2,2,6,6-tetramethyl-3,5-heptanedione. Complexes of Formula II wherein Y is a halogen can be purchased commercially. Complexes of Formula II wherein Y is hydrogen or an organic group can be prepared by reduction of the metal halides or reaction of the metal halides with Grignard reagents. Complexes of Formula II wherein Y is an amine group can be prepared by reaction of a metal halide with lithium dialkylamide.

Various precursor compounds can be used in various combinations (typically, mixtures of compounds of Formula I or mixtures of compounds of Formula II, but preferably no mixtures of compounds of Formulas I and II), optionally with one or more organic solvents (particularly for CVD processes), to form a precursor composition. The precursor compounds may be liquids or solids at room temperature (preferably, they are liquids at the vaporization temperature). Typically, they are liquids sufficiently volatile to be employed using known vapor deposition techniques. However, as solids they may also be sufficiently volatile that they can be vaporized or sublimed from the solid state using known vapor deposition techniques. If they are less volatile solids, they are preferably sufficiently soluble in an organic solvent or have melting points below their decomposition temperatures such that they can be used in flash vaporization, bubbling, microdroplet formation techniques, etc. Herein, vaporized precursor compounds may be used either alone or optionally with vaporized molecules of other precursor compounds or optionally with vaporized solvent molecules, if used. As used herein, “liquid” refers to a solution or a neat liquid (a liquid at room temperature or a solid at room temperature that melts at an elevated temperature). As used herein, “solution” does not require complete solubility of the solid but may allow for some undissolved solid, as long as there is a sufficient amount of the solid delivered by the organic solvent into the vapor phase for chemical vapor deposition processing. If solvent dilution is used in deposition, the total molar concentration of solvent vapor generated may also be considered as a inert carrier gas.

The solvents that are suitable for this application (particularly for a CVD process) can be one or more of the following: aliphatic hydrocarbons or unsaturated hydrocarbons (C3-C20, and preferably C5-C10, cyclic, branched, or linear), aromatic hydrocarbons (C5-C20, and preferably C5-C10), halogenated hydrocarbons, silylated hydrocarbons such as alkylsilanes, alkylsilicates, ethers, polyethers, thioethers, esters, lactones, ammonia, amides, amines (aliphatic or aromatic, primary, secondary, or tertiary), polyamines, nitrites, cyanates, isocyanates, thiocyanates, silicone oils, alcohols, or compounds containing combinations of any of the above or mixtures of one or more of the above. The compounds are also generally compatible with each other, so that mixtures of variable quantities of the precursor compounds will not interact to significantly change their physical properties.

For this invention, preferably no reaction gas is employed to minimize oxidation of the substrate (typically silicon) to its oxide (typically silicon dioxide). The “diketo”-containing precursor compound(s) provide the source oxygen.

The precursor compounds can be vaporized in the presence of an inert carrier gas if desired. Additionally, an inert carrier gas can be used in purging steps in an ALD process. The inert carrier gas is typically selected from the group consisting of nitrogen, helium, argon, and combinations thereof. In the context of the present invention, an inert carrier gas is one that does not interfere with the formation of the metal-containing layer. Whether done in the presence of a inert carrier gas or not, the vaporization is preferably done in the absence of oxygen to avoid oxygen contamination of the layer (e.g., oxidation of silicon to form silicon dioxide).

The deposition process for this invention is a vapor deposition process. Vapor deposition processes are generally favored in the semiconductor industry due to the process capability to quickly provide highly conformal layers even within deep contacts and other openings. Chemical vapor deposition (CVD) and atomic layer deposition (ALD) are two vapor deposition processes often employed to form thin, continuous, uniform, metal-containing (preferably dielectric) layers onto semiconductor substrates. Using either vapor deposition process, typically one or more precursor compounds are vaporized in a deposition chamber and optionally combined with one or more reaction gases to form a metal-containing layer onto a substrate. It will be readily apparent to one skilled in the art that the vapor deposition process may be enhanced by employing various related techniques such as plasma assistance, photo assistance, laser assistance, as well as other techniques.

The final layer (preferably, a dielectric layer) formed preferably has a thickness in the range of about 10 Å to about 500 Å. More preferably, the thickness of the metal-containing layer is in the range of about 30 Å to about 80 Å.

In most vapor deposition processes, the precursor compound(s) are typically reacted with an oxidizing or reducing reaction gas (e.g., water vapor, oxygen or ammonia) at elevated temperatures to form the oxide layer. However, in the practice of this invention, no such reaction gas is needed as the precursor compound(s) provide the source of oxygen needed. However, oxidizing gases, such as O₂, O₃, H₂O, and H₂O₂, can be used if desired.

Chemical vapor deposition (CVD) has been extensively used for the preparation of metal-containing layers, such as dielectric layers, in semiconductor processing because of its ability to provide highly conformal and high quality dielectric layers at relatively fast processing times. The desired precursor compounds are vaporized and then introduced into a deposition chamber containing a heated substrate with optional reaction gases and/or inert carrier gases. In a typical CVD process, vaporized precursors are contacted with reaction gas(es) at the substrate surface to form a layer (e.g., dielectric layer). The single deposition cycle is allowed to continue until the desired thickness of the layer is achieved.

Typical CVD processes generally employ precursor compounds in vaporization chambers that are separated from the process chamber wherein the deposition surface or wafer is located. For example, liquid precursor compounds are typically placed in bubblers and heated to a temperature at which they vaporize, and the vaporized liquid precursor compound is then transported by an inert carrier gas passing over the bubbler or through the liquid precursor compound. The vapors are then swept through a gas line to the deposition chamber for depositing a layer on substrate surface(s) therein. Many techniques have been developed to precisely control this process. For example, the amount of precursor material transported to the deposition chamber can be precisely controlled by the temperature of the reservoir containing the precursor compound and by the flow of an inert carrier gas bubbled through or passed over the reservoir.

Preferred embodiments of the precursor compounds described herein are particularly suitable for chemical vapor deposition (CVD). The deposition temperature at the substrate surface is preferably held at a temperature in a range of about 100° C. to about 600° C., more preferably in the range of about 200° C. to about 500° C. The deposition chamber pressure is preferably maintained at a deposition pressure of about 0.1 torr to about 10 torr. The partial pressure of precursor compounds in the inert carrier gas is preferably about 0.001 torr to about 10 torr.

Several modifications of the CVD process and chambers are possible, for example, using atmospheric pressure chemical vapor deposition, low pressure chemical vapor deposition (LPCVD), plasma enhanced chemical vapor deposition (PECVD), hot wall or cold wall reactors or any other chemical vapor deposition technique. Furthermore, pulsed CVD can be used, which is similar to ALD (discussed in greater detail below) but does not rigorously avoid intermixing of percursor and reactant gas streams. Also, for pulsed CVD, the deposition thickness is dependent on the exposure time, as opposed to ALD, which is self-limiting (discussed in greater detail below).

A typical CVD process may be carried out in a chemical vapor deposition reactor, such as a deposition chamber available under the trade designation of 7000 from Genus, Inc. (Sunnyvale, Calif.), a deposition chamber available under the trade designation of 5000 from Applied Materials, Inc. (Santa Clara, Calif.), or a deposition chamber available under the trade designation of Prism from Novelus, Inc. (San Jose, Calif.). However, any deposition chamber suitable for performing CVD may be used.

Alternatively, and preferably, the vapor deposition process employed in the methods of the present invention is a multi-cycle ALD process. Such a process is advantageous (particularly over a CVD process) in that in provides for optimum control of atomic-level thickness and uniformity to the deposited layer (e.g., dielectric layer) and to expose the metal precursor compounds to lower volatilization and reaction temperatures to minimize degradation. Typically, in an ALD process, each reactant is pulsed sequentially onto a suitable substrate, typically at deposition temperatures of about 25° C. to about 400° C. (preferably about 150° C. to about 300° C.), which is generally lower than presently used in CVD processes. Under such conditions the film growth is typically self-limiting (i.e., when the reactive sites on a surface are used up in an ALD process, the deposition generally stops), insuring not only excellent conformality but also good large area uniformity plus simple and accurate thickness control. Due to alternate dosing of the precursor compounds and/or reaction gases, detrimental vapor-phase reactions are inherently eliminated, in contrast to the CVD process that is carried out by continuous coreaction of the precursors and/or reaction gases. (See Vehkamaki et al, “Growth of SrTiO₃ and BaTiO₃ Thin Films by Atomic Layer Deposition,” Electrochemical and Solid-State Letters, 2(10):504-506 (1999)).

A typical ALD process includes exposing an initial substrate to a first chemical species (e.g., a silicon precursor compound) to accomplish chemisorption of the species onto the substrate. Theoretically, the chemisorption forms a monolayer that is uniformly one atom or molecule thick on the entire exposed initial substrate. In other words, a saturated monolayer. Practically, chemisorption might not occur on all portions of the substrate. Nevertheless, such an imperfect monolayer is still a monolayer in the context of the present invention. In many applications, merely a substantially saturated monolayer may be suitable. A substantially saturated monolayer is one that will still yield a deposited layer exhibiting the quality and/or properties desired for such layer.

The first species is purged from over the substrate and a second chemical species (e.g., a different precursor compound) is provided to react with the first monolayer of the first species. The second species is then purged and the steps are repeated with exposure of the second species monolayer to the first species. In some cases, the two monolayers may be of the same species. As an option, the second species can react with the first species, but not chemisorb additional material thereto. That is, the second species can cleave some portion of the chemisorbed first species, altering such monolayer without forming another monolayer thereon. Also, a third species or more may be successively chemisorbed (or reacted) and purged just as described for the first and second species. Optionally, the second species (or third or subsequent) can include at least one reaction gas if desired.

Purging may involve a variety of techniques including, but not limited to, contacting the substrate and/or monolayer with a carrier gas and/or lowering pressure to below the deposition pressure to reduce the concentration of a species contacting the substrate and/or chemisorbed species. Examples of carrier gases include N₂, Ar, He, etc. Purging may instead include contacting the substrate and/or monolayer with any substance that allows chemisorption by-products to desorb and reduces the concentration of a contacting species preparatory to introducing another species. The contacting species may be reduced to some suitable concentration or partial pressure known to those skilled in the art based on the specifications for the product of a particular deposition process.

ALD is often described as a self-limiting process, in that a finite number of sites exist on a substrate to which the first species may form chemical bonds. The second species might only bond to the first species and thus may also be self-limiting. Once all of the finite number of sites on a substrate are bonded with a first species, the first species will often not bond to other of the first species already bonded with the substrate. However, process conditions can be varied in ALD to promote such bonding and render ALD not self-limiting. Accordingly, ALD may also encompass a species forming other than one monolayer at a time by stacking of a species, forming a layer more than one atom or molecule thick.

The described method indicates the “substantial absence” of the second precursor (i.e., second species) during chemisorption of the first precursor since insignificant amounts of the second precursor might be present. According to the knowledge and the preferences of those with ordinary skill in the art, a determination can be made as to the tolerable amount of second precursor and process conditions selected to achieve the substantial absence of the second precursor.

Thus, during the ALD process, numerous consecutive deposition cycles are conducted in the deposition chamber, each cycle depositing a very thin metal-containing layer (usually less than one monolayer such that the growth rate on average is from about 0.2 to about 3.0 Angstroms per cycle), until a layer of the desired thickness is built up on the substrate of interest. The layer deposition is accomplished by alternately introducing (i.e., by pulsing) precursor compound(s) into the deposition chamber containing a semiconductor substrate, chemisorbing the precursor compound(s) as a monolayer onto the substrate surfaces, and then reacting the chemisorbed precursor compound(s) with the other co-reactive precursor compound(s). The pulse duration of precursor compound(s) and inert carrier gas(es) is sufficient to saturate the substrate surface. Typically, the pulse duration is from about 0.1 to about 5 seconds, preferably from about 0.2 to about 1 second.

In comparison to the predominantly thermally driven CVD, ALD is predominantly chemically driven. Accordingly, ALD is often conducted at much lower temperatures than CVD. During the ALD process, the substrate temperature is maintained at a temperature sufficiently low to maintain intact bonds between the chemisorbed precursor compound(s) and the underlying substrate surface and to prevent decomposition of the precursor compound(s). The temperature is also sufficiently high to avoid condensation of the precursor compounds(s). Typically the substrate temperature is kept within the range of about 25° C. to about 400° C. (preferably about 150° C. to about 300° C.), which is generally lower than presently used in CVD processes. Thus, the first species or precursor compound is chemisorbed at this temperature. Surface reaction of the second species or precursor compound can occur at substantially the same temperature as chemisorption of the first precursor or, less preferably, at a substantially different temperature. Clearly, some small variation in temperature, as judged by those of ordinary skill, can occur but still be a substantially same temperature by providing a reaction rate statistically the same as would occur at the temperature of the first precursor chemisorption. Chemisorption and subsequent reactions could instead occur at exactly the same temperature.

For a typical ALD process, the pressure inside the deposition chamber is kept at about 10⁻⁴ torr to about I torr, preferably about 10⁻⁴ torr to about 0.1 torr. Typically, the deposition chamber is purged with an inert carrier gas after the vaporized precursor compound(s) have been introduced into the chamber and/or reacted for each cycle. The inert carrier gas(es) can also be introduced with the vaporized precursor compound(s) during each cycle.

The reactivity of a precursor compound can significantly influence the process parameters in ALD. Under typical CVD process conditions, a highly reactive compound may react in the gas phase generating particulates, depositing prematurely on undesired surfaces, producing poor films, and/or yielding poor step coverage or otherwise yielding non-uniform deposition. For at least such reason, a highly reactive compound might be considered not suitable for CVD. However, some compounds not suitable for CVD are superior ALD precursors. For example, if the first precursor is gas phase reactive with the second precursor, such a combination of compounds might not be suitable for CVD, although they could be used in ALD. In the CVD context, concern might also exist regarding sticking coefficients and surface mobility, as known to those skilled in the art, when using highly gas-phase reactive precursors, however, little or no such concern would exist in the ALD context.

After layer formation on the substrate, an annealing process can be optionally performed in situ in the deposition chamber in a nitrogen atmosphere or oxidizing atmosphere. Preferably, the annealing temperature is within the range of about 400° C. to about 1000° C. Particularly after ALD, the annealing temperature is more preferably about 400° C. to about 750° C., and most preferably about 600° C. to about 700° C. The annealing operation is preferably performed for a time period of about 0.5 minute to about 60 minutes and more preferably for a time period of about 1 minute to about 10 minutes. One skilled in the art will recognize that such temperatures and time periods may vary. For example, furnace anneals and rapid thermal annealing may be used, and further, such anneals may be performed in one or more annealing steps.

As stated above, the use of the complexes and methods of forming films of the present invention are beneficial for a wide variety of thin film applications in semiconductor structures, particularly those using high dielectric materials. For example, such applications include gate dielectrics and capacitors such as planar cells, trench cells (e.g., double sidewall trench capacitors), stacked cells (e.g., crown, V-cell, delta cell, multi-fingered, or cylindrical container stacked capacitors), as well as field effect transistor devices.

A specific example of where a dielectric layer is formed according to the present invention is a capacitor construction. Exemplary capacitor constructions are described with reference to FIGS. 1-3. Referring to FIG. 1, a semiconductor wafer fragment 10 includes a capacitor construction 25 formed by a method of the present invention. Wafer fragment 10 includes a substrate 12 having a conductive diffusion area 14 formed therein. Substrate 12 can include, for example, monocrystalline silicon. An insulating layer 16, typically borophosphosilicate glass (BPSG), is provided over substrate 12, with a contact opening 18 provided therein to diffusion area 14. A conductive material 20 fills contact opening 18, with material 20 and oxide layer 18 having been planarized as shown. Material 20 might be any suitable conductive material, such as, for example, tungsten or conductively doped polysilicon. Capacitor construction 25 is provided atop layer 16 and plug 20, and electrically connected to node 14 through plug 20.

Capacitor construction 25 includes a first capacitor electrode 26, which has been provided and patterned over node 20. Examplary materials include conductively doped polysilicon, Pt, Ir, Rh, Ru, RuO₂, IrO₂, RhO₂. A capacitor dielectric layer 28 is provided over first capacitor electrode 26. The materials of the present invention can be used to form the capacitor dielectric layer 28. Preferably, if first capacitor electrode 26 includes polysilicon, a surface of the polysilicon is cleaned by an in situ HF dip prior to deposition of the dielectric material. An exemplary thickness for layer 28 in accordance with 256 Mb integration is 100 Angstroms.

A diffusion barrier layer 30 is provided over dielectric layer 28. Diffusion barrier layer 30 includes conductive materials such as TiN, TaN, metal silicide, or metal silicide-nitride, and can be provided by CVD, for example, using conditions well known to those of skill in the art. After formation of barrier layer 30, a second capacitor electrode 32 is formed over barrier layer 30 to complete construction of capacitor 25. Second capacitor electrode 32 can include constructions similar to those discussed above regarding the first capacitor electrode 26, and can accordingly include, for example, conductively doped polysilicon. Diffusion barrier layer 30 preferably prevents components (e.g., oxygen) from diffusing from dielectric material 28 into electrode 32. If, for example, oxygen diffuses into a silicon-containing electrode 32, it can undesirably form SiO₂, which will significantly reduce the capacitance of capacitor 25. Diffusion barrier layer 30 can also prevent diffusion of silicon from metal electrode 32 to dielectric layer 28.

FIG. 2 illustrates an alternative embodiment of a capacitor construction. Like numerals from FIG. 1 have been utilized where appropriate, with differences indicated by the suffix “a”. Wafer fragment 10 a includes a capacitor construction 25 a differing from the construction 25 of FIG. 2 in provision of a barrier layer 30 a between first electrode 26 and dielectric layer 28, rather than between dielectric layer 28 and second capacitor electrode 32. Barrier layer 30 a can include constructions identical to those discussed above with reference to FIG. 1.

FIG. 3 illustrates yet another alternative embodiment of a capacitor construction. Like numerals from FIG. 1 are utilized where appropriate, with differences being indicated by the suffix “b” or by different numerals. Wafer fragment 10 b includes a capacitor construction 25 b having the first and second capacitor plate 26 and 32, respectively, of the first described embodiment. However, wafer fragment 10 b differs from wafer fragment 10 of FIG. 2 in that wafer fragment 10 b includes a second barrier layer 40 in addition to the barrier layer 30. Barrier layer 40 is provided between first capacitor electrode 26 and dielectric layer 28, whereas barrier layer 30 is between second capacitor electrode 32 and dielectric layer 28. Barrier layer 40 can be formed by methods identical to those discussed above with reference to FIG. 1 for formation of the barrier layer 30.

In the embodiments of FIGS. 1-3, the barrier layers are shown and described as being distinct layers separate from the capacitor electrodes. It is to be understood, however, that the barrier layers can include conductive materials and can accordingly, in such embodiments, be understood to include at least a portion of the capacitorr electrodes. In particular embodiments an entirety of a capacitor electrode can include conductive barrier layer materials.

A system that can be used to perform vapor deposition processes (chemical vapor deposition or atomic layer deposition) of the present invention is shown in FIG. 4. The system includes an enclosed vapor deposition chamber 110, in which a vacuum may be created using turbo pump 112 and backing pump 114. One or more substrates 116 (e.g., semiconductor substrates or substrate assemblies) are positioned in chamber 110. A constant nominal temperature is established for substrate 116, which can vary depending on the process used. Substrate 116 may be heated, for example, by an electrical resistance heater 118 on which substrate 116 is mounted. Other known methods of heating the substrate may also be utilized.

In this process, precursor compounds 160 (e.g., a refractory metal precursor compound and an ether) are stored in vessels 162. The precursor compounds are vaporized and separately fed along lines 164 and 166 to the deposition chamber 110 using, for example, an inert carrier gas 168. A reaction gas 170 may be supplied along line 172 as needed. Also, a purge gas 174, which is often the same as the inert carrier gas 168, may be supplied along line 176 as needed. As shown, a series of valves 180-185 are opened and closed as required.

The following examples are offered to further illustrate the various specific and preferred embodiments and techniques. It should be understood, however, that many variations and modifications may be made while remaining within the scope of the present invention, so the scope of the invention is not intended to be limited by the examples. Unless specified otherwise, all percentages shown in the examples are percentages by weight.

EXAMPLE Example 1 Atomic Layer Deposition of (Y,Al)₂O₃

The deposition of (Y,Al)₂O₃ was carried out using alternating pulses of Y(thd)₃ (available from Strem Chemical Co., Newburyport, Mass.) and Al(Et)₃ (available from Rohm & Haas, Danvers, Mass.) vapor in an ALD process. The precursors were held at 190° C. and 50° C., respectively. The substrate had a top layer of 1500 Angstroms of doped polysilicon and was held at 300° C. during 400 cycles. The film formed was approximately 400 Angstroms thick and remained amorphous (as determined by XRD) even after a 750° C. anneal in nitrogen for 1 minute. The ratio of Yttrium to Aluminum was determined by XPS and further identified by ICP spectroscopy to have an approximate stoichiometry of Y_(0.1)Al_(1.9)O₃. TEM showed an amorphous (Y,Al)₂O₃ with no apparent SiO₂ at the interface. Electrical measurements were performed on the material by sputtering platinum electrodes on top of the film through a hard mask. The dielectric constant was 34 at 1 kHz and leakage was 8×10⁻⁹ A/cm².

The complete disclosures of the patents, patent documents, and publications cited herein are incorporated by reference in their entirety as if each were individually incorporated. Various modifications and alterations to this invention will become apparent to those skilled in the art without departing from the scope and spirit of this invention. It should be understood that this invention is not intended to be unduly limited by the illustrative embodiments and examples set forth herein and that such examples and embodiments are presented by way of example only with the scope of the invention intended to be limited only by the claims set forth herein as follows. 

1. A method of manufacturing a semiconductor structure, the method comprising: providing a semiconductor substrate or substrate assembly; providing at least one precursor compound of the formula L_(n)M¹O_(x)(keto)_(y)(Formula I) and at least one precursor compound of the formula M²Y_(z)(Formula II), wherein: M¹ and M² are the same metal; each L group is a neutral or anionic supporting ligand; each “keto” is independently a diketonate or ketoimine ligand; each Y group is independently a halogen (X), R¹, or an amine of the formula (NR²R³), wherein each R¹is an organic moiety, and each R² and R³ is independently hydrogen or an organic group; n is 0 to 5; x is 0 to 3; y is 1 to 5 and is dependent on the oxidation state of M¹ and on the value of n; and z is at least one and is dependent on the oxidation state of M^(2;) and contacting the precursor compounds to form a metal oxide layer on one or more surfaces of the semiconductor substrate or substrate assembly using a vapor deposition process.
 2. The method of claim 1 wherein the semiconductor substrate or substrate assembly is a silicon wafer.
 3. The method of claim 1 wherein the metal oxide layer is a dielectric layer.
 4. The method of claim 1 wherein M¹and M² are selected from the group of metals consisting of Groups IIA, IIIA, IVA, IVB, VA, VB, VIIIB, IB and the lanthanides.
 5. The method of claim 4 wherein M¹ and M² are selected from the group of metals consisting of Sr, Ba, Y, the lanthanides, Ti, Zr, Hf, Nb, Ta, Al, and Si.
 6. The method of claim 5 wherein M¹ and M² are selected from the group of metals consisting of Sr, Ba, Y, La, Ce, Pr, Gd, Ti, Al, and Si.
 7. The method of claim 6 wherein M¹ and M² are selected from the group of metals consisting of La, Ce, Pr, Gd, Al, and Si.
 8. The method of claim 1 wherein each R¹ is an organic moiety having 1-10 carbon atoms, and R² and R³ are each independently organic groups having 1-10 carbon atoms.
 9. The method of claim 1 wherein at least one Y is R¹ and each R¹is independently a (C1-C4) organic moiety.
 10. The method of claim 1 wherein at least one Y is NIR²R³ and R² and R³ are each independently a (C1-C4) organic group.
 11. The method of claim 1 wherein the “keto” ligand is of the formula (Formula IV):

wherein Z is O or NR⁷ and each R (R⁴, R⁵, R⁶, and R⁷) is independently hydrogen or an organic group.
 12. The method of claim 11 wherein Z is oxygen.
 13. The method of claim 1 wherein n is 0 to 2 and y is 2 to
 3. 14. The method of claim 1 wherein the compound of Formula II is of the formula M²X_(r)R_(s) ¹, wherein r +s is dependent on the oxidation state of M².
 15. The method of claim 1 wherein L is absent.
 16. A method of forming a metal oxide layer on a substrate, the method comprising: providing a substrate; providing at least one precursor compound of the formula L_(n)M¹O_(x)(keto)_(y) (Formula I) and at least one precursor compound of the formula M²Y_(z)(Formula II), wherein: M¹ and M² are the same metal; each L group is a neutral or anionic supporting ligand; each “keto” is independently a diketonate or ketoimine ligand; each Y group is independently a halogen (X), R¹, or an amine of the formula (NR²R³), wherein each R¹is an organic moiety, and each R² and R³ is independently hydrogen or an organic group; n is 0 to 5; x is 0 to 3; y is 1 to 5 and is dependent on the oxidation state of M¹and on the value of n; and z is at least one and is dependent on the oxidation state of M^(2;) and contacting the precursor compounds to form a metal oxide layer on the substrate using a vapor deposition process.
 17. The method of claim 16 wherein the metal oxide layer has a thickness of about 30 Å to about 80 Å. 